Effect of filler-filler interaction on rheological behaviour of natural rubber compounds filled with both carbon black and silica

Rubber compounds are reinforced with fillers such as carbon black and silica. In general, filled rubber compounds show smooth rheological behaviour in measurement of Mooney viscosity or Mooney scorch time. Variation in rheological behaviour was studied in terms of the filler composition using natural rubber compounds filled with both carbon black and silica (carbon black/silica = 60/20,40/ 40, and 20/60 phr). The compound filled with carbon black/silica of 60/20 phr showed normal rheological behaviour. However, The compounds filled with carbon black/silica of 40/40 and 20/60 phr showed abnormal rheological behaviour, in which the viscosity increased suddenly and then decreased at a certain point during the measurement. The abnormal behaviour was explained by the strong filler-filler interaction of silica. Moreover, the abnormal rheological behaviour was displayed more clearly as the storage time of compounds is increased.