Examination of Au/SnO₂ core-shell architecture nanoparticle for low temperature gas sensing applications

Au/SnO₂ core-shell structure nanoparticles (NPs) were synthesized using two methods, microwave and conventional precipitation. In both cases, the size of the Au core was 12-18 nm and the thickness of the SnO ₂ shell was 8-12 nm. The particle size of SnO₂ synthesized using the microwave and precipitation method was 3-5 nm and 1-2 nm, respectively. Upon heating to 400-600 °C, both particles maintained their core-shell morphology but the smaller SnO₂ particles prepared using the precipitation method were more sintered. The resistance changes in films of these particles were measured as a function of CO concentration. The Au/SnO ₂ particles prepared using the microwave method showed higher sensor response than those prepared using the precipitation method, even providing a significant signal at testing temperatures approaching ambient conditions, thereby affording a new class of material for gas sensing. Both sets of core-shell particles showed higher sensor response than the SnO₂ nanoparticles. The role of the Au core as a catalyst in improving the adsorption and oxidation of CO gas is important for improving the low temperature response. In addition, the maintenance of the size of SnO₂ in the microwave method during sintering contributed to the higher response towards CO sensing.