Fluorinated Organic A-Cation Enabling High-Performance Hysteresis-Free 2D/3D Hybrid Tin Perovskite Transistors

2D tin-based perovskites have gained considerable attention for use in diverse optoelectronic applications, such as solar cells, lasers, and thin-film transistors (TFTs), owing to their good stability and optoelectronic properties. However, their intrinsic charge-transport properties are limited, and the insulating bulky organic ligands hinder the achievement of high-mobility electronics. Blending 3D counterparts into 2D perovskites to form 2D/3D hybrid structures is a synergistic approach that combine the high mobility and stability of 3D and 2D perovskites, respectively. In this study, reliable p-channel 2D/3D tin-based hybrid perovskite TFTs comprising 3D formamidinium tin iodide (FASnI₃) and 2D fluorinated 4-fluoro-phenethylammonium tin iodide ((4-FPEA)₂SnI₄) are reported. The optimized FPEA-incorporated TFTs show a high hole mobility of 12 cm² V⁻¹ s⁻¹, an on/off current ratio of over 10⁸, and a subthreshold swing of 0.09 V dec⁻¹ with negligible hysteresis. This excellent p-type characteristic is compatible with n-type metal-oxide TFT for constructing complementary electronics. Two procedures of antisolvent engineering and device patterning are further proposed to address the key concern of low-performance reproducibility of perovskite TFTs. This study provides an alternative A-cation engineering method for achieving high-performance and reliable tin-halide perovskite electronics.