Mechanical, morphological and thermal properties of short carbon and aramid fibres-filled bromo-isobutylene-isoprene rubber vulcanised with 4, 4’ bis(maleimido)diphenylmethane

This paper describes the use of a combination of 4, 4’ bis(maleimido)diphenylmethane and ZnO as a high-temperature processable vulcanising agent for the short aramid and carbon fibre-filled bromo-isobutylene-isoprene rubber. The fibre breakage analysis, cure characteristics, mechanical, thermal and morphological properties of the composites were evaluated with different fibre loading. The fibre breakage analyses revealed that the aramid fibres have good length retention property compared to carbon fibres. The morphological analysis of the extracted aramid fibres showed severe surface roughness primarily due to fibrillation after shear mixing. The fibrillated aramid fibres lead to aggregation and poor dispersion of the fibres in the rubber matrix. However, fibrillation imparted surface roughness and increased surface area on the aramid fibres which improved the fibre–matrix interaction via mechanical anchoring. On the other hand, the carbon fibre-filled composite showed poor fibre–matrix interaction and inferior strength and modulus.