title = "Preparation of Ti-Mo-Si alloy powders from Ti alloy scraps",
abstract = "Low-oxygen content Ti-Mo-Si powders were manufactured using two types of ternary Ti alloy ingots which were prepared by vacuum arc melting of Ti-Mo scrap with Si. The weight ratio of Ti-Mo scrap was Ti:Mo = 9:1 and Si contents in two alloy ingots were 1 and 2\%. The alloy powders were prepared by the Hydrogenation-dehydrogenation and the subsequent solid-state deoxidation methods. The deoxidation process effectively reduced the initial oxygen content from 3, 350 ppm to 1, 700 ppm. In addition, the high-temperature oxidation resistance was enhanced by adding Si to Ti-Mo alloys. Thermal gravimetric analysis showed that the weight gain by oxidation was reduced from 8.85\% for Ti-Mo to 7.5\% for Ti-Mo-Si at 1, 500 °C.",
author = "Roh, \{Ki Min\} and Oh, \{Jung Min\} and Wonbaek Kim and Suh, \{Chang Youl\} and Hanjung Kwon",
year = "2014",
language = "English",
series = "Euro PM 2014 Congress and Exhibition, Proceedings",
publisher = "European Powder Metallurgy Association (EPMA)",
booktitle = "Euro PM 2014 Congress and Exhibition, Proceedings",
note = "Euro PM 2014 International Conference and Exhibition ; Conference date: 21-09-2014 Through 24-09-2014",
}