Synthesis and electrochemical properties of nano-composite IrO₂/TiO₂ anode catalyst for SPE electrolysis cell

A composite catalyst of nano-grade IrO₂/TiO₂ powder is synthesized by Adams’ fusion method for reducing overvoltage of solid polymer electrolyte (SPE) cell and cost-down of noble metal catalyst, simultaneously. The IrO₂/TiO₂ catalysts, which has a porous composite nanostructure, are prepared according to molar ratio of Ir and Ti element with a specific surface area of 34.1–55.3 m² g⁻¹. It is found that crystal structure of TiO₂ is more dominated by the rutile phase than by Anatase. For a SPE system, total catalyst loading of anode which made of TiO₂ and IrO₂ is prepared as low as 0.77 mg cm⁻² or less, in which the loading amount of the IrO₂ only is set to 0.6 mg cm⁻² or less. The anode catalyst layer of about 10 ㎛ thickness is coated on the membrane (Nafion 212) for the membrane electrode assembly (MEA) by the decal method. The strong adhesion between the catalyst electrode the membrane is observed by Scanning electron microscopy (SEM). Linear sweep voltammetry (LSV) results shows that the nano-composite IrO₂/TiO₂ catalysts has better oxygen evolution reaction (OER) than that of the synthesis IrO₂ only. Finally, the IrO₂/TiO₂ catalysts is applied as anode electrode for SPE cells and it is observed that in spite of the lower loading amount of the IrO₂ less than 0.5 mg cm⁻², working voltage of 1.68 V is observed at a current density of 1 A cm⁻² and operating temperature of 80 °C.