Systematic analysis of palladium-graphene nanocomposites and their catalytic applications in Sonogashira reaction

Graphene has been modified with palladium nanoparticles (Pd NPs) to develop high performance catalysts for the Sonogashira cross coupling reaction. In this research, graphite oxide (GO) sheets exfoliated from graphite were impregnated with Pd(OAc)₂ to prepare Pd²⁺/GO. Thermal treatments of the Pd²⁺/GO in H₂ flow at 100°C produced Pd/graphene (Pd/G) nanocomposites. TEM images show that Pd NPs were distributed quite uniformly on the graphene sheet without obvious aggregation, and the mean size of Pd NPs was determined to be less than 2nm in diameter. Morphological and chemical structures of the GO, Pd²⁺/GO, and Pd/G were investigated using FT-IR, XRD, XPS, and XAFS. The resulting Pd/G showed excellent catalytic efficiency in the Sonogashira reaction and offers significant advantages over inorganic supported catalysts such as simple recovery and recycling. Finally, deactivation process of the Pd/G in recycling was investigated. We believe that the remarkable reactivity of the Pd/G catalyst toward the Sonogashira reaction is attributed to the high degree of the Pd NP dispersion and thus the increased low coordination numbers of smaller Pd NPs.