Abstract
We report solution properties of the blend solutions of poly(vinyl alcohol) (PVA) and poly(ethylene glycol) (PEG)-POSS telechelic and its corresponding hybrid nanofibers prepared by electrospinning. The morphologies, microstructures, and wettability of the resulting PVA/PEG3.4k-POSS hybrid nanofibers are studied. The morphologies of the resultant PVA/PEG3.4k-POSS nanofibers are regular with the fiber diameter ranging from 610∈± ∈110 to 810∈±∈280 nm. When the content of PEG3.4k-POSS telechelic increases above 20 wt.%, the beaded fiber morphologies are observed due to severe aggregations of the PEG3.4k-POSS telechelics as well as increased viscosity at higher concentration. In addition, the solution properties of pure PEG3.4k-POSS telechelic solution (ca. 3-5 wt.%) and PVA/PEG3.4k-POSS solutions blended with PVA are explored, and found to show the reversible turbid-to-transparent transition behavior with respect to the solution temperature. Water contact angle measurement of the PVA/PEG3.4k-POSS nanofiber membranes demonstrates an enhanced hydrophobic nature due to the incorporated POSS moieties.
| Original language | English |
|---|---|
| Pages (from-to) | 863-870 |
| Number of pages | 8 |
| Journal | Colloid and Polymer Science |
| Volume | 289 |
| Issue number | 8 |
| DOIs | |
| State | Published - 2011.06 |
Keywords
- Electrospinning
- Nanofibers
- Poly(vinyl alcohol) (PVA)
- Polyhedral oligosilsesquioxane (POSS)
- Telechelic
- Wettability
Quacquarelli Symonds(QS) Subject Topics
- Materials Science
- Engineering - Petroleum
- Engineering - Chemical
- Chemistry
Fingerprint
Dive into the research topics of 'Transition behaviors and hybrid nanofibers of poly(vinyl alcohol) and polyethylene glycol-POSS telechelic blends'. Together they form a unique fingerprint.Cite this
- APA
- Author
- BIBTEX
- Harvard
- Standard
- RIS
- Vancouver